| FASTENERS -SCREWS, BOLTS AND NUTS FOR TOUGHEST USE | ||||
| Material | Size | Length | Specification | Manufacturer |
| Aluminum 6061-T6 Fasteners | M 02 to M 160 | 3 mm | DIN | GKW |
| to | ISO | Unbrako | ||
| 200 mm | JIS | Kundan | ||
| GB | APL | |||
| IS | Sundaram Precision | |||
| BS | Infasco | |||
| ASTM | EBY Fastener Etc. | |||
| Aluminum 6061-T6 Threads: | METRIC, BSW, BSF, UNC, UNF or as required | |||
| Aluminum 6061-T6 In Form of: | Hex | |||
| Square | ||||
| Round | ||||
| Threading as per Gauge Etc. | ||||
| Head drive: | Phillips, Slotted, Phillips/Slot, Six-Lobe, etc | |||
| Aluminum 6061-T6 Packing: | IN BULK :canton/pallet, Small Boxs/carton/ pallet, or customer request | |||
| Aluminum 6061-T6 Test Certificate: | Manufacturer Test Certificate as per EN 10204 / 3.1 | |||
| Aluminum 6061-T6 finishing: | Natural, Nickle Plated, Silver Plated, Tin Plated. | |||
| Geometry, Dacroment, anodizing, nickel plated, plated zinc-nickel, Stainless steel: | ||||
| Passivated | ||||
| Production process | M2-M24: Cold Froging, hot forging M24-M100, | |||
| machining and CNC for Customized connecting element | ||||
| Aluminum 6061-T6 Origin and service-region: | European | |||
| Origin of Aluminum 6061-T6 are Western European. However projects with eastern origin are possible on request. | ||||
| Surface Coating: | Hot Dipped Galvanizing Fasteners | |||
| Phosphate Fasteners | ||||
| Teflon Fasteners | ||||
| Ptfe Coated Fasteners | ||||
| Xylon Fasteners | ||||
| Zinc Fasteners | ||||
| Cadmium Fasteners | ||||
| Our Fastener plant is equipped with various testing facilities like Tensile Testing Machine also known as tension testing. We also conduct other tests like Hardness Test, IGC Test, Positive Material Identification Test to ensure that all the product going out of our manufacturing plant are the best in terms of quality. | ||||
| Physical Properties | Metric | English | Comments |
| Density | 2.7 g/cc | 0.0975 lb/in³ | AA; Typical |
| Mechanical Properties | |||
| Hardness, Brinell | 95 | 95 | AA; Typical; 500 g load; 10 mm ball |
| Hardness, Knoop | 120 | 120 | Converted from Brinell Hardness Value |
| Hardness, Rockwell A | 40 | 40 | Converted from Brinell Hardness Value |
| Hardness, Rockwell B | 60 | 60 | Converted from Brinell Hardness Value |
| Hardness, Vickers | 107 | 107 | Converted from Brinell Hardness Value |
| Ultimate Tensile Strength | 310 MPa | 45000 psi | AA; Typical |
| Tensile Yield Strength | 276 MPa | 40000 psi | AA; Typical |
| Elongation at Break | 12 % | 12 % | AA; Typical; 1/16 in. (1.6 mm) Thickness |
| Elongation at Break | 17 % | 17 % | AA; Typical; 1/2 in. (12.7 mm) Diameter |
| Modulus of Elasticity | 68.9 GPa | 10000 ksi | AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. |
| Notched Tensile Strength | 324 MPa | 47000 psi | 2.5 cm width x 0.16 cm thick side-notched specimen, Kt = 17. |
| Ultimate Bearing Strength | 607 MPa | 88000 psi | Edge distance/pin diameter = 2.0 |
| Bearing Yield Strength | 386 MPa | 56000 psi | Edge distance/pin diameter = 2.0 |
| Poisson's Ratio | 0.33 | 0.33 | Estimated from trends in similar Al alloys. |
| Fatigue Strength | 96.5 MPa | 14000 psi | AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen |
| Fracture Toughness | 29 MPa-m½ | 26.4 ksi-in½ | KIC; TL orientation. |
| Machinability | 50 % | 50 % | 0-100 Scale of Aluminum Alloys |
| Shear Modulus | 26 GPa | 3770 ksi | Estimated from similar Al alloys. |
| Shear Strength | 207 MPa | 30000 psi | AA; Typical |