H13 Fasteners
We are manufacturing high-class H13 Fasteners in India
You can buy H13 Fasteners, H13 Hot Work Tool Steels Nuts, H13 Hot work Tool Steels Bolts, H13 Hot work Tool Steels Screws, H13 Hot work Tool Steels washers for perfect connection & critical applications, excellent pricing and extensive size range of H13 Fasteners.
Grand Metal Corporation is a most renowned H13 Fasteners suppliers in Aerospace, Engine & Turbine Engineering. It is widely used in industries such as aerospace, defence, automotive, petrochemical, waste processing, marine and pharmaceutical sectors. We supply custom H13 Fasteners created in precise time. We provide H13 Fasteners with NACE 3.1 Certification.
| FASTENERS -SCREWS, BOLTS AND NUTS FOR TOUGHEST USE |
| Material |
Size |
Length |
Specification |
Manufacturer |
| H13 Fasteners |
M 02 to M 160 |
3 mm |
DIN |
GKW |
| to |
ISO |
Unbrako |
| 200 mm |
JIS |
Kundan |
| |
GB |
APL |
| |
IS |
Sundaram Precision |
| |
BS |
Infasco |
| |
ASTM |
EBY Fastener Etc. |
| H13 Hot Work Tool Threads: |
METRIC, BSW, BSF, UNC, UNF or as required |
| H13Fasteners In Form of: |
Hex |
| Square |
| Round |
| Threading as per Gauge Etc. |
| Head drive: |
Phillips, Slotted, Phillips/Slot, Six-Lobe, etc |
| H13 Hot Work Tool Packing: |
IN BULK :canton/pallet, Small Boxs/carton/ pallet, or customer request |
| H13 Hot Work Tool Test Certificate: |
Manufacturer Test Certificate as per EN 10204 / 3.1 |
| H13 Hot Work Tool finishing: |
Natural, Nickle Plated, Silver Plated, Tin Plated. |
| Geometry, Dacroment, anodizing, nickel plated, plated zinc-nickel, Stainless steel: |
| Passivated |
| Production process |
M2-M24: Cold Froging, hot forging M24-M100, |
| machining and CNC for Customized connecting element |
| H13 Hot Work Tool Origin and service-region: |
European |
| Origin of H13 Fasteners are Western European. However projects with eastern origin are possible on request. |
| Grades: |
A2Fasteners, H11Fasteners,H13 Fasteners,T75 Fasteners |
| Our Fastener plant is equipped with various testing facilities like Tensile Testing Machine also known as tension testing. We also conduct other tests like Hardness Test, IGC Test, Positive Material Identification Test to ensure that all the product going out of our manufacturing plant are the best in terms of quality. |
H13 Fasteners Useful Info
H13 Tool Steel – Chromium Hot-Work Steels
H13 chromium hot-work steel is widely used in hot and cold work tooling applications. Due to its excellent combination of high toughness and fatigue resistance H13 is used more than any other tool steel in tooling applications.
AISI Type H13 Hot Work Tool Steel, air or oil quenched from 995-1025°C
Subcategory: Hot Work Steel; Metal; Tool Steel
Key Words: UNS T20813, ASTM A681, FED QQ-T-570, BS 4659 BH13, BS 4659 H13, BS EN ISO 4957 :2000 X40CrMoV5-1, Werkstoff 1.2344
| Component |
Wt. % |
| C |
0.32 – 0.4 |
| Cr |
5.13 – 5.25 |
| Fe |
Min 90.95 |
| Mo |
1.33 – 1.4 |
| Si |
1 |
| V |
1 |
Material Notes:
Iron content is calculated as a remainder. High hardenability, excellent wear resistance and hot toughness. H13 has good thermal shock resistance and will tolerate some water cooling in service. Nitriding will improve hardness, but can diminish shock resistance if hardened layer is too thick. Electroslag Remelted (ESR) H13 has greater homogeneity and an exceptionally fine structure, resulting in improved machinability, polishability and high temperature tensile strength.
Applications: hot work applications: pressure die casting tools, extrusion tools, forging dies, hot shear blades, stamping dies, plastic molds. ESR H13 is great for aluminium die-casting tools and pastic mold tools requiring a very high polish.
Weldability: Pre and Post-heating recommended, can be welded with oxy-acetylene, inert shielded gas and shielded metal arc; Filler should be similar to the base metal.
| Physical Properties |
Metric |
English |
Comments |
| Density |
7.8 g/cc |
0.282 lb/in³ |
|
| Mechanical Properties |
| Hardness, Knoop |
570 |
570 |
Converted from Rockwell C Hardness. |
| Hardness, Rockwell C |
52 – 54 |
52 – 54 |
air or oil quenched and tempered at 510°C (950°F) and 540°C (1000°F). |
| Hardness, Rockwell C |
51 – 53 |
51 – 53 |
air or oil quenched and tempered at 565°C (1050°F). |
| Hardness, Rockwell C |
49 – 51 |
49 – 51 |
air or oil quenched and tempered at 595°C (1100°F). |
| Hardness, Rockwell C |
45 – 47 |
45 – 47 |
air or oil quenched and tempered at 620°C (1150°F). |
| Hardness, Rockwell C |
39 – 41 |
39 – 41 |
air or oil quenched and tempered at 650°C (1200°F). |
| Hardness, Rockwell C |
31 – 33 |
31 – 33 |
air or oil quenched and tempered at 675°C (1250°F). |
| Hardness, Rockwell C |
28 – 30 |
28 – 30 |
air or oil quenched and tempered at 705°C (1300°F). |
| Hardness, Rockwell C |
51 – 53 |
51 – 53 |
air quenched from 1025°C (1875°F) or oil quenched from 1010°C (1850°F) with no temper, or tempered for 1 hour at 315°C (600°F), 425°C (800°F), and 480°C (900°F). |
| Hardness, Vickers |
549 |
549 |
Converted from Rockwell C Hardness. |
| Tensile Strength, Ultimate |
1990 MPa |
289000 psi |
|
| Tensile Strength, Yield |
1650 MPa |
239000 psi |
|
| Elongation at Break |
9% |
9% |
|
| Modulus of Elasticity |
210 GPa |
30500 ksi |
at 20°C |
| Bulk Modulus |
140 GPa |
20300 ksi |
Typical for steel. |
| Poisson's Ratio |
0.3 |
0.3 |
Calculated |
| Machinability |
50% |
50% |
Based on 1% carbon steel. as 100% machinability |
| Shear Modulus |
81 GPa |
11700 ksi |
Estimated from elastic modulus |
| Thermal Properties |
| CTE, linear 20°C |
11 µm/m-°C |
6.11 µin/in-°F |
25 – 95°C |
| CTE, linear 250°C |
11.5 µm/m-°C |
6.39 µin/in-°F |
25 – 205ºC |
| CTE, linear 500°C |
12.4 µm/m-°C |
6.89 µin/in-°F |
25 – 540°C |
| Heat Capacity |
0.46 J/g-°C |
0.11 BTU/lb-°F |
from 0-100°C (32-212°F) |
| Thermal Conductivity |
24.3 W/m-K |
169 BTU-in/hr-ft²-°F |
at 215°C; 24.4 W/m-K at 350°C, 24.3 at 475°C; 24.7 at 605°C |
| Descriptive Properties |
| Annealing Temperature |
850 – 870°C for 4 hours |
furnace cool 20°C per hour max. |
| Stress Relieving Temperature |
600 – 650°C for 2 hours (approx.) |
cool in still air; always stess relief before hardening. |