| Material | Size | Length | Specification | Manufacturer |
| MP35N Fasteners | M 02 to M 160 | 3 mm | DIN | GKW |
| to | ISO | Unbrako | ||
| 200 mm | JIS | Kundan | ||
| GB | APL | |||
| IS | Sundaram Precision | |||
| BS | Infasco | |||
| ASTM | EBY Fastener Etc. |
| MP35N Threads: | METRIC, BSW, BSF, UNC, UNF or as required |
| Standard: | DIN 933, DIN 931, ANSI, JIS standards |
| MP35N Fasteners In Form of: | Hex |
| Square | |
| Round | |
| Threading as per Gauge Etc. | |
| Head drive: | Phillips, Slotted, Phillips/Slot, Six-Lobe, etc |
| MP35N Packing: | IN BULK :canton/pallet, Small Boxs/carton/ pallet, or customer request |
| MP35N Test Certificate: | Manufacturer Test Certificate as per EN 10204 / 3.1 |
| Property Class: | For Bolts & Screws: A2-70, A2-80, A4-70, A4-80, F593C, F593D, F593G, F593H |
| For Nuts: A2-70, A2-80, A4-70, A4-80, F594C, F594D, F594G, F594H, A2-035, A4-040 | |
| For SHCS: F837B, F837C, F837E, F837 | |
| For Threaded Rods: A2-70, A2-80, A4-70, A4-80, F593C, F593D, F593G, F593H, B8, B8M CL1 & CL2 | |
| MP35N finishing: | Zinc (yellow, white, blue, black), black oxide, |
| Geometry, Dacroment, anodizing, nickel plated, plated zinc-nickel, Stainless steel: Passivated | |
| Self-Colour, Hot Dip Galvanised (HDG), Bright Zinc Plated (BZP), Sherardized, Stainless Steel, Mechanically Applied coating and some special one like DACROMET | |
| Production process | M2-M24: Cold Froging, hot forging M24-M100, |
| machining and CNC for Customized connecting element | |
| MP35N Origin and service-region: | European |
| Origin of MP35N Fasteners are Western European. However projects with eastern origin are possible on request. | |
| Grades: | Inconel 600 Fasteners, Inconel 601 Fasteners, Inconel 625 Fasteners, Inconel 718 Fasteners, Inconel X750 Fasteners, Incoloy 800H Fasteners, Incoloy 825 Fasteners, Monel 400 Fasteners, Monel 405 Fasteners, Monel K-500 Fasteners, Hastelloy C276 Fasteners, MP35N Fasteners, Nickel 200 Fasteners, Waspaloy Fasteners |
| Surface Coating: | Hot Dipped Galvanizing Fasteners |
| Phosphate Fasteners | |
| Teflon Fasteners | |
| Ptfe Coated Fasteners | |
| Xylon Fasteners | |
| Zinc Fasteners | |
| Cadmium Fasteners |
| Physical Properties | Metric | English | Comments |
| Density | 8.43 g/cc | 0.305 lb/in3 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 931 MPa | 135000 psi | |
| Tensile Strength, Yield | 414 MPa @Strain 0.200 % | 60000 psi @Strain 0.200 % | |
| Elongation at Break | 70.00% | 70.00% | |
| Reduction of Area | 70.00% | 70.00% | |
| Modulus of Elasticity | 232.8 GPa | 33770 ksi | |
| Shear Modulus | 83.36 GPa | 12090 ksi |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0001033 ohm-cm | 0.0001033 ohm-cm | Room Temp. 1.154E-4 Ohm-cm at 538°C |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 93.0 °C | 7.11 µin/in-°F @Temperature 69.8 - 199 °F | |
| 14.8 µm/m-°C @Temperature 21.0 - 316 °C | 8.22 µin/in-°F @Temperature 69.8 - 601 °F | ||
| 15.7 µm/m-°C @Temperature 21.0 - 538 °C | 8.72 µin/in-°F @Temperature 69.8 - 1000 °F | ||
| Thermal Conductivity | 11.2 W/m-K | 77.7 BTU-in/hr-ft2-°F | at room Temp. 17.0 W/m-K at 316°C. 23.4 W/m-K at 649°C. |
| Melting Point | 1315 - 1440 °C | 2399 - 2620 °F | |
| Solidus | 1315 °C | 2399 °F | |
| Liquidus | 1440 °C | 2620 °F |
| Component Elements Properties | Metric | English | Comments |
| Boron, B | 0.01% | 0.01% | |
| Carbon, C | <= 0.025 % | <= 0.025 % | |
| Chromium, Cr | 19.0 - 21.0 % | 19.0 - 21.0 % | |
| Cobalt, Co | 33.00% | 33.00% | as remainder |
| Iron, Fe | <= 1.0 % | <= 1.0 % | |
| Manganese, Mn | <= 0.15 % | <= 0.15 % | |
| Molybdenum, Mo | 9.0 - 10.5 % | 9.0 - 10.5 % | |
| Nickel, Ni | 33.0 - 37.0 % | 33.0 - 37.0 % | |
| Phosphorous, P | <= 0.015 % | <= 0.015 % | |
| Silicon, Si | <= 0.15 % | <= 0.15 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % | |
| Titanium, Ti | <= 1.0 % | <= 1.0 % |