304L Stainless Steel Bolts
We are recounted as a manufacturer, exporter & providers of 304L stainless steel bolts, to be had in a variety or grades, substances, and finishes, in metric and inch sizes. We are full line fastener distributor that specialize in industrial merchandise for corporations involved in system manufacturing, mining, oil refineries, chemical production, metal and aluminium manufacturing, utilities and transportation, and business production.
Grand Metal holds a range of 304L Stainless steel bolts from carbon steel, stainless steel and high nickel alloy -f467 NiCu 400 (monel) and industrial 18-eight/304, 316 stainless steel. We supply 304L stainless steel bolts at extremely compatible price.
Grades and Specification of 304L Stainless Steel Bolts
Range of Stainless Steel Fasteners product 304L Stainless Steel Bolts, Hexagon head bolt, Hexagon head screw, Round head square neck bolt, Hexagon socket head cap screw in full thread and half thread, Hexagon wood screw, Hexagon socket button head screw, Hexagon socket button flange screw, Hexagon socket counter sunk head cap screw in full thread and half thread, square nuts, square weld nuts, hexagon weld nuts, thick nyloc nuts, hexagon flange nuts, threaded rods, dowel screws and many more. These products are availed as per Indian and international standards.
Other Details of 304L Stainless Steel Bolts
| Product Material |
304L Stainless Steel Bolts |
| 304L Stainless Steel Bolts Size |
M02 to M33 |
| Available Length |
3 Mm to 300Mm |
| Standards |
ISO & DIN |
Material Type
| For Bolts & Screws |
A2-70, A2-80, A4-70, A4-80, F593C, F593D, F593G, F593H |
| For Nuts |
A2-70, A2-80, A4-70, A4-80, F594C, F594D, F594G, F594H, A2-035, A4-040 |
| For SHCS |
F837B, F837C, F837E, F837 |
| For Threaded Rods |
A2-70, A2-80, A4-70, A4-80, F593C, F593D, F593G, F593H, B8, B8M CL1 & CL2 |
Our Stainless Steel Fastener plant is equipped with various testing facilities like Tensile Testing Machine also known as tension testing. We also conduct other tests like Hardness Test, IGC Test, Positive Material Identification Test to ensure that all the product going out of our manufacturing plant are the best in terms of quality.
| Fasteners ASTM Grades |
| ASTM A193 Grade B5, ASTM A193 Grade B6, ASTM A193 Grade B7, ASTM A193 Grade B16, ASTM A193 Grade B8, ASTM A193 Grade B8C, ASTM A193 Grade B8M, ASTM A193 Grade B8T, ASTM A193 Grade B8, ASTM A193 Grade B8C, ASTM A193 Grade B8M, ASTM A193 Grade B8T, ASTM A320 Grade L7, ASTM A320 Grade L7A, ASTM A320 Grade L7B, ASTM A320 Grade LC7, ASTM A320 Grade L43, ASTM A320 Grade B8, ASTM A320 Grade B8C, ASTM A320 Grade B8T, ASTM A320 Grade B8F, ASTM A320 Grade B8M, ASTM A320 Grade B8, ASTM A320 Grade B8C, ASTM A320 Grade B8F, ASTM A320 Grade B8M, ASTM A320 Grade B8T, SAE J429 Grade 5, ASTM A449, SAE J429 Grade 5.1, SAE J429 Grade 5.2, ASTM A325 Type 1, ASTM A325 Type 2, ASTM A325 Type 3, ASTM A354 Grade BB, ASTM A354 Grade BC, SAE J429 Grade 7, SAE J429 Grade 8, ASTM A354 Grade BD, SAE J429 Grade 8.1, ASTM A490 |
Further Useful info of 304L Stainless Steel Bolt more details
Both 304 stainless steel and 304L stainless steel offer a standard reason stainless steel with excellent resistance to atmospheric corrosion, to many organic and inorganic chemicals and to food and liquids.
The distinction among 304 and 304L stainless steel is that 304L has a .03 max carbon and is ideal for welding while 304 has a mid-range level of carbon. 304 and 304L are austenitic alloys, which means that a nonmagnetic strong solution of ferric carbide or carbon in iron is used in giving this stainless steel its corrosion-resistant properties.
General Application
Chemical equipment and piping, heat exchanger components, dairy and food handling equipment and utensils, cryogenic vessels and components, architectural and structural applications exposed to non-marine atmospheres
Stainless Steel 304L Bolt Chemical Composition- Per ASTM A240
| Element |
Type 304 |
Type 304L |
| Carbon |
0.7Max |
0.030Max |
| Manganese |
2.00 Max |
2.00Max |
| Sulphur |
0.030 Max |
0.030 Max |
| Phosphorus |
0.045 Max |
0.045 Max |
| Silicon |
0.75 Max |
0.75 Max |
| Chromium |
17.5 to 19.5 Max |
18 to 20 Max |
| Nickel |
8.0 to 10.5 Max |
8.0 to 12.0 Max |
| Nitrogen |
0.1 Max |
0.1 Max |
Mechanical Properties – Per ASTM A 240, A666
| Type |
Yield Strength 0.2% offset (KSI) |
Tensile Strength (KSI) |
% Elongation (2"Gauge length ) |
Hardness Rockwell |
| 304 Ann |
30 Min |
75 Min |
40 Min |
HRB 92 Max |
| 304 1/4 Hard |
75 Min |
125 Min |
12 Min |
HRC 25-32 |
| 304 1/2 Hard |
110 Min |
150 Min |
7 Min |
HRC 32-37 |
| 304L Ann |
25 Min |
70 Min |
40 Min |
HRB 92 Max |
| 304L 1/4 Hard |
75 Min |
125 Min |
12 Min |
HRC 25-32 |
| 304L 1/2 Hard |
110 Min |
150 Min |
6 Min |
HRC 32-37 |
Processing
Types 304 and 304L cannot be hardened by thermal treatment. Annealing: Heat to 1850° F to 2050 ° F and cool at sufficiently high rates through 1500°F to 800°F to avoid precipitation of chromium carbides. Stress Relief Annealing: Cold worked parts should be stress relieved at 750°F for ½ to 2 hours.
Forming
Annealed Types 304 and 304L can be fabricated by roll forming, deep drawing, bending and most other fabrication techniques. Due to the high work hardening rate of these materials, intermediate anneals maybe required to successfully fabricate the part.
Welding
Types 304 and 304L are weld able by most fusion or resistance welding techniques. If filler metal is required, Type 308 is normally used. Type 304L should be used in heavier sections to reduce the occurrence of carbide precipitation in the heat affected region adjacent to the weld pool
Corrosion
Types 304 and 304L provides corrosion resistance in a wide range of moderately oxidizing and reducing conditions, fresh water and non-marine applications.